Aloi	Pembinaan Strand Standard, mm	Rintangan,Ω/m	Diameter Helai Nominal, mm	Meter per Kilo
NiCr 80/20	18×0.544+1×0.574	0.252-0.278	2.67	26
NiCr 80/20	19×0.61	0.205-0.250	3.05
NiCr 80/20	18×0.523+1×0.574	0.271-0.299	2.67	30
NiCr 80/20	19×0.574	0.227-0.251	2.87	25
NiCr 80/20	36×0.385+1×0.45	0.265-0.293	2.76	26
NiCr 60/15	19×0.508	0.286-0.318	2.54
NiCr 60/15	18×0.523+1×0.574	0.276-0.305	2.76	30
Ni200/Ni201	19×0.574	0.019-0.021	2.87	21

N6	Chromel C, Ni 60, N6, HAI-NiCr 60, Tophet C, Resistohm 60, Cronifer II,
	Elektroloy, Nichrome, Aloi C, Ni 6, MWS-675, Stablohm 675
N7	Ni 70, Chromel 70/30, N7, Hytemco, HAI-NiCr 70, Balco, Tophet 30,
	Resistohm 70, Cronix 70, Stablohm 710
N8	Chromel A, Ni 80, N8, Nichrome V, HAI-NiCr 80, Tophet A, Resistohm
	80, Cronix 80, Protoloy, Ni 8, Aloi A, MWS-650, Stablohm 650

Hartanah/Gred		Cr20Ni80	Cr30Ni70	Cr15Ni60	Cr20Ni35	Cr20Ni30
Komposisi kimia utama	Ni	Rehat	Rehat	55.0-61.0	34.0-37.0	30.0-34.0
	Cr	20.0-23.0	28.0-31.0	15.0-18.0	18.0-21.0	18.0-21.0
	Fe	≤ 1.0	≤ 1.0	Rehat	Rehat	Rehat
Maks. temp perkhidmatan berterusan. daripada unsur		1200	1250	1150	1100	1100
Kerintangan pada 20oC (μ Ω · m)		1.09	1.18	1.12	1.04	1.04
Ketumpatan (g/cm3)		8.4	8.1	8.2	7.9	7.9
Kekonduksian terma(KJ/m· h· oC)		60.3	45.2	45.2	43.8	43.8
Pekali pengembangan garisan(α × 10-6/oC)		18	17	17	19	19
Takat lebur (lebih kurang )( oC)		1400	1380	1390	1390	1390
Pemanjangan semasa pecah (%)		> 20	> 20	> 20	> 20	> 20
Struktur mikrografik		austenit	austenit	austenit	austenit	austenit
Sifat magnetik		bukan magnet	bukan magnet	bukan magnet	bukan magnet	bukan magnet